- Silicone Water Repellent
- Water Based Water Repellent
- Gypsum Water Repellent
- Silane Impregnant
- Waterproofing Admixture
- Super Hydrophobic Water and Oil Repellent
- Waterproofing Coatings
- Silicone rubber coating RJ-DN121
- Anti-graffiti waterproof coating RJ-AG01
- Masonry Water Repellent RJ-WP40
- Ceramic Water Repellent
- Distribution Agent Wanted
- Personal Care
- Agricultural Adjuvant
- Textile Auxiliaries
- Pump Oils
- Silane Coupling Agent
- Silicone Foam Stabilizer
- Silicone Fluids
- Silicone Sealant
- Silane Crosslinking Agent
- PFPE Oils
- Silicone Rubber
- Silicone Antifoam
- Silicone Intermediate
- CAS Index
Anti-graffiti waterproof coating RJ-AG01※MSDS Download Be Without TDS Download Inquiry
RJ-AG01 is a kind of high performance two component fluorine silicon anti graffiti nano coating.The main components of the coating is fluorine silicon resin and nano materials. After the coating cured, it will have extreme low surface tension and excellent anti graffiti effect.
|Surface curing time||≤2h|
|Anti adhesion (180°peel strength)||≤0.1 N/mm|
|Acid/Alkali/Salt resistance test 240h||Pass|
|Ageing resistance test 1000h||Pass|
v Extreme low surface tension.
v Excellent ageing resistance.
v Good adhesion with other primers coating such as epoxy, polyurethane, acrylate.
v Various colour
It can make the “paper advertising”which use glue and other stickers very easy to peel off from the wall.Ink and water-based paint are difficult to attach on the surface of the coating, even if a little mark can be easily removed.Oil-based paint can also be be easily removed by cleaning agents such as alcohol, acetone.
The substrate surface should be dry and clean.If applied on concrete wall, the surface pH should under 10(pH＜10), and coated with a closed primer.
Mix A( main component):B(curing agent)=8:1 (by weight),stand for about 15 minutes before the application.Do not do construction below 5 ℃ .After mix A and B,the mixture coating should be used up within 3 hours.
Available in 20kg drums.
The product should be stored in a shady, dry place with the temperature 0°C-40°C freezing should be avoided.
Avoid from acid, alkali chemical materials and other impurities.