Addition type electric silicone rubber RJ-0235AB

 

Description

RJ-0235AB is two-component solid silicone rubber, short curing time, good mechanical properties, no pollutants released during the curing process, safety, environmental protection, mainly applied for cold-shrink cable accessories such as the three fingerstall, indoor terminal and a variety of insulation accessories, sheathes, etc.

 

 

Features and Advantages

v Transparent paste

v Translucent silicone rubber

v    Addition polymerization

v    Modification by active components

v    Excellent electric insulation

v    Vulcanized system

Suitable for mold and extrusion process

Easily pigmentation

Safe ,environment-friendly

v    Very wide service temperature range

High tear strength

High volume resistivity

 

Technical Date

Properties

Value

Appearance

Transparent cream

Specific gravity (25℃) 

1.170

Durometer hardness (Shore,A)

38-45

Tensile strength at break (MPa)

≥7.0

Tear strength (kN/m)

≥30.0

Elongation at break (%)

≥700

Permanent set at break (%)

≤4.8

Electrical resistivity (Ω · cm)

Dielectric constant (1KHz)

Dielectric strength(kV/mm)

25

Dissipation factor

≤0.02

 

Note: These values are not intended for use in preparing specification.

 

 

Application

RJ-0235AB is mainly applied for cold-shrink cable accessories such as the three fingerstall, indoor terminal and a variety of insulation accessories, sheathes, etc.

 

 

Packing

RJ-0235AB is available in 25kg paper box or other packing on request.

 

Storage

The product is a non-dangerous product. In storage and transportation, avoiding exposure in sun and rain is required.

 

 

Shelf life

Original characteristics remain intact for 1 year from the date of production at room temperature in seal-tight condition, it is strongly recommended that the containers are sealed tightly after use each time.

 