This RJL-wc-3401 series of products are platinum catalyzed two-component elastomer silicone gel suitable for wound care, with a mixture ratio of 1:1.
Typical Physical Properties
Typical properties of the uncured rubber: | |||||
Property | method | Value | |||
Appearance | A-part | Transparent | |||
B-part | Transparent | ||||
Viscosity (20°C) | DIN 53018 | A-part | 300-500 mPa•s | ||
B-part | 300-500 mPa•s | ||||
The pot-life of the mixture of the two components (closed vessel) at 20 ºC is five days. Increased temperatures reduce the pot-life. Typical properties of the Vulcanisate: Mixing ratio of components A : B = 1 : 1. Vulcanisation: 10-15 min. at 110 ºC | |||||
Potlife（hours，at 23℃） | ＞24 | ||||
Curing Time（min，at 120℃） | 10 | ||||
Penetration (mm/10 hollow cone 62.5g) | DIN ISO 2137 | 230 | |||
Typical properties are only for reference.