Description

This RJL-3370 series of products are platinum catalyzed two-component liquid silicone rubber suitable for injection molding process, with a mixture ratio of 1:1. It has good adhesiveness to plastic parts, especially suitable for producing a high strength composite of silicone rubber and plastic materials


Technical Index

Typical Physical Properties

Typical properties of the uncured rubber:

Property

method

Value

Appearance


A-part

Transparent


B-part

Transparent

Viscosity   (20°C)

DIN 53018

A-part

4500000mPa•s

B-part

8500000mPa•s

The pot-life of the   mixture of the two components (closed vessel) at 20 ºC is 3 days.

Increased temperatures   reduce the pot-life.

Typical properties of   the Vulcanisate:   Mixing ratio of   components A : B = 1 : 1.

Vulcanisation: 10 min. at 150 ºC

Shore   A hardness

DIN   53 505

70±2

Density


1.13±0.02g/cm3

Tensile   strength

DIN   53 504 52

7.0 MPa

Elongation   at break

DIN   53 504 52

250 %

Tear   strength

ASTM   D 624 die B

25 N/mm

90°peel   strength


1.5 KN/m






Typical properties are only for reference.


Application
This product can be used in variety of applications, including:
Suitable for producing a high strength composite of silicone rubber and plastic materials.
Packing
RJL-3370 liquid silicone rubber is currently available in 20 kg pail-kits and 200 kg drum-kits.