Description
The RJH-2300 series are flam-retardant HCR for molding, extruding and calendering compression.
Technical Index
Typical general characteristics
Property | Inspection method | Value |
Appearance | white | |
Density @23℃ | ISO 1183-1 A | 1.45g/cm3 |
Hardness Shore A | DIN 53505 | 60 |
Tensile strength | DIN 53504 S 1 | 6.5Mpa |
Elongation at break | DIN 53504 S 1 | 336% |
Tear Strength | ASTM D 624 B | 16KN/m |
Compression set | DIN ISO 815-B | 35% |
Flame-retardant | ANSI/UL-94-1985 | 94V0 |
Heat stability | ||
Properties after aging 10days @250℃ | ||
Hardness Shore A | DIN 53505 | 66 |
Tensile strength | DIN 53504 S 1 | 4.8Mpa |
Elongation at break | DIN 53504 S 1 | 180% |
Note:
• Ratio of curing agent DBPMH(95%): 0.6%
• Cure condition: 175℃×10Min
• Post cure condition: 200℃×4h
• The samples for compression set and rebound elasticity are after post-cured.
Application
This product can be used in variety of applications, including:
Suitable for all kinds of products that need to be used in high temperature and flame-retardant environment.